Product Introduction:
Light weight polyester putty (car filler) is provided by FOSHAN SHUNDE HIMENS INDUSTRIAL CO., LTD,a major School Furniture supplier in Furniture & Furnishing wholesale industry in China.You can check out the specification of Light weight polyester putty (car filler) below or get any optional result clicking into the following keywords Light weight polyester putty (car filler) and you can check the authentications and testimonials of Light weight polyester putty (car filler) .
Description:
307 Light Polyester Putty
Ingredients:
Unsaturated polyesters resins, modified resin, color pigment, stuffing, anti sediment materials, auxiliary agent and firming agent mixing ratio 100:2.
The ash is exquisite and has excellent construction performance, which can well tamp the sand holes left after rough scraping with polyester putty. Also, polyester putty finely scraped enjoys quick drying, good sanding property and adhesion. It is mainly applicable to the filling and leveling up as well as decoration of the deficiencies such as sand holes, pinholes and shrink holes on the surface of polyester putty before closing the undercoat in the painting dressing of cars, so as to strengthen the flatness and smoothness of the surface of polyester putty. And it meets the requirements of flatness and smoothness etc. on the appearance of top coating.
Main technical standard:
Item Index Testing Standard
Outward appearance The color is unanimous, and there are no visible particles by naked eye, and being rather exquisite Visual examination
Air drying Meet the customers requirements GB/T1728-79
Consistency 9-12cm (except for the specialities) GB/T1749
Scratching performance Good handling, no curling
Burnishing performance Burnishing easy, extraction powder is fast.
Resistance to high temperature There is no bubbling and cracking under baking at 120 degree centigrade after drying
There is no bubbling and cracking under baking at 80 degree centigrade after gelling
Pliability ≤50mm GB/T1748
Impact Strength ≥13kg.cm (or 35kg.cm Not falling off) GB/T1732
Adhesive force ≥65Kg/1.2cm2 GB/T5210
Reference for construction:
1. Evenly mix the main ash and firming agent with the proportion being 100:2 (make the color unanimous), and using up them within the gelation time.
2.Scratch the putty which has already finely mixed on the primer paint of double components after burnishing or the surface of cold-rolled sheet which has already been finished processing. If the
-
-
-
-